Synthetic nanopores have a large potential in biotechnology, where they can be applied e.g. as filters, sensors for biomolecules or as single-molecule detectors and analyzers. For all these applications it is important to understand the pores’ ionic transport characteristics and to be able to influence them at will, depending on the desired application. In this context it is highly desirable to be able to control the pores’ surface properties, i.e. functionalize them, to match specific requirements concerning hydrophobicity, selectivity or interactions with various biomolecules. The track-etching technique, which is based on irradiation with swift heavy ions and subsequent chemical etching, is a well established method to create nanopores of various geometries in polymer foils [1]. Single, conical pores in polyethylene terephthalate, polyimide and polycarbonate show asymmetric current-voltage characteristics (a phenomenon called rectification) as well as permselectivity [1,2,3]. These properties, which are basically resulting from electrostatic interactions, have been addressed by a number of theoretical approaches [3,4,5,6], including a model based on the Poisson and Nernst-Planck (PNP) equations [4,7,8], which provides good agreement between experiments and calculations. The polymeric substrate of the pores opens the possibility to directly chemically modify the functional groups present at the inner pore walls by a variety of methods. For example amines can be covalently coupled to the carboxyl groups present on the etched surfaces of most polymeric pores, resulting in control over the surface charge of the pore [9,10]. By this method, any molecule containing free amino groups can potentially be attached to the surfaces of these pores, allowing the creation of desired interactions between the pore walls and molecules present in the electrolyte solution. [1]Apel P., Korchev Y., Siwy Z., Spohr R. and Yoshida M., Diode-like single-ion track membrane prepared by electro-stopping. textit{Nucl. Instrum. Methods Phys. Res., Sect. B} textbf{184} 337–46 (2001). [2]Siwy Z., Ion-current rectification in nanopores and nanotubes with broken symmetry. textit{Adv. Funct. Mater.} textbf{16} 735 (2006). [3]Siwy Z. and Ful`i nski A., A nanodevice for rectification and pumping ions. textit{Am. J. Phys.} textbf{72} 567 (2004). [4]Cervera J., Schiedt B., Neumann R., Mafé S. and Ramírez P., Ionic conduction, rectification, and selectivity in single conical nanopores textit{J. Chem. Phys.} textbf{124} 104706 (2006). [5]Kosi`nska I., How the asymmetry of internal potential influences the shape of I-V characteristic of nanochannels. textit{J. Chem. Phys.} textbf{124} 244707 (2006). [6]Liu Q., Wang Y., Guo W., Ji H., Xue J. and Ouyang Q., Asymmetric properties of ion transport in a charged conical nanopore. textit{Phys. Rev. E} textbf{75} 051201–1–6 (2007). [7]Cervera J., Alcaraz A., Schiedt B., Neumann R. and Ramírez P., Asymmetric selectivity of synthetic conical nanopores probed by reversal potential measurements. textit{J. Phys. Chem. C}, Accepted. [8]Cervera J., Schiedt B. and Ramírez P., A Poisson/Nernst-Planck model for ionic transport through synthetic conical nanopores. textit{Europhys. Lett.} textbf{71} 35–41 (2005). [9]Vlassiouk I. and Siwy Z. S., Nanofluidic diode. textit{Nano Lett.} textbf{7} 552–56 (2007). [10]Ali M., Schiedt B., Healy K., Neumann R. and Ensinger W., Modifying the surface charge of single track-etched conical nanoporesin polyimide. textit{Nanotechnology} textbf{19 }085713 (2007).
Gesellschaft für Schwerionenforschung (GSI), Planckstr. 1, D-64291 Darmstadt, Germany